Sensitivity Analysis of Production Variables of Geopolymer Cement Concrete to Mechanical and Durability Characteristics

Search for this publication on Google Scholar
TREJO, M. A. R. I. A. (2016). Sensitivity Analysis of Production Variables of Geopolymer Cement Concrete to Mechanical and Durability Characteristics. Unc Charlotte Electronic Theses And Dissertations.
Download PDF

Analytics

84 views ◎
56 downloads ⇓


Abstract

Geopolymer cement is an alternative binder manufactured from fly ashes that can fully replace portland cement in traditional reinforced concrete applications. As a viable material for precast components, geopolymer features very rapid strength development and the ability to be prepared using typical concrete equipment. This study focused on a sensitivity analysis of three base mixture designs of geopolymer cement concrete (GCC) with compressive strengths ranging from 1500-6000 psi (10.3-414 MPa). The fresh concrete properties including slump flow, air content, and temperature were measured and correlated to the mechanical properties including the compressive strength, modulus of rupture, and modulus of elasticity. The main purpose of the sensitivity analysis is to determine the level of influence of typical production variables on the resulting mechanical properties of the concrete. The production variables, such as, water to cementitious materials ratio (w/cm), curing temperature, and curing duration are each known to impact the compressive strength and elastic properties of GCC. Regression analysis was used to determine the level of influence of each production variable on mechanical properties. The interactions between changes in the production variables were also studied to determine if a combination of variables may have a greater net impact on the mechanical properties of the concrete. From the analysis, we find that as we adjust production variables we can influence the resulting compressive strength. These relationships have been illustrated with the regression models. This study also characterized the freeze thaw durability of GCC. The study resulted in improved freeze-thaw durability of GCC for a 2% to 3% air content range compared to the same range in portland cement concrete (PCC).

Details
Author

TREJO, MARIA

Title

Sensitivity Analysis of Production Variables of Geopolymer Cement Concrete to Mechanical and Durability Characteristics

Physical Description

1 online resource (197 pages) : PDF

Date

2016

Degree Granting Institution

University of North Carolina at Charlotte

Abstract

Geopolymer cement is an alternative binder manufactured from fly ashes that can fully replace portland cement in traditional reinforced concrete applications. As a viable material for precast components, geopolymer features very rapid strength development and the ability to be prepared using typical concrete equipment. This study focused on a sensitivity analysis of three base mixture designs of geopolymer cement concrete (GCC) with compressive strengths ranging from 1500-6000 psi (10.3-414 MPa). The fresh concrete properties including slump flow, air content, and temperature were measured and correlated to the mechanical properties including the compressive strength, modulus of rupture, and modulus of elasticity. The main purpose of the sensitivity analysis is to determine the level of influence of typical production variables on the resulting mechanical properties of the concrete. The production variables, such as, water to cementitious materials ratio (w/cm), curing temperature, and curing duration are each known to impact the compressive strength and elastic properties of GCC. Regression analysis was used to determine the level of influence of each production variable on mechanical properties. The interactions between changes in the production variables were also studied to determine if a combination of variables may have a greater net impact on the mechanical properties of the concrete. From the analysis, we find that as we adjust production variables we can influence the resulting compressive strength. These relationships have been illustrated with the regression models. This study also characterized the freeze thaw durability of GCC. The study resulted in improved freeze-thaw durability of GCC for a 2% to 3% air content range compared to the same range in portland cement concrete (PCC).

Genre

masters theses

Subjects--Topics

Civil engineering

Degree

M.S.

Keywords

Compressive Strength
Durability
Fly Ash
Freeze Thaw
Geopolymer Cement Concrete
Sensitivity

Subject Area

Civil Engineering

Advisor(s)

Tempest, Brett

Committee Members

Gergely, Janos
Cavalline, Tara

Degree Note

Thesis (M.S.)--University of North Carolina at Charlotte, 2016.

Rights Statement

This Item is protected by copyright and/or related rights. You are free to use this Item in any way that is permitted by the copyright and related rights legislation that applies to your use. For other uses you need to obtain permission from the rights-holder(s). For additional information, see http://rightsstatements.org/page/InC/1.0/.

Rights Holder Information

Copyright is held by the author unless otherwise indicated.

Identifier

TREJO_uncc_0694N_11303

Permalink

http://hdl.handle.net/20.500.13093/etd:1650