Optical performance of random anti-reflection structured surfaces (rARSS) on spherical lenses

Search for this publication on Google Scholar
Taylor, C. (2016). Optical performance of random anti-reflection structured surfaces (rARSS) on spherical lenses. Unc Charlotte Electronic Theses And Dissertations.
Download PDF

Analytics

347 views ◎
157 downloads ⇓


Abstract

Random anti-reflection structured surfaces (rARSS) have been reported to improve transmittance of optical-grade fused silica planar substrates to values greater than 99%. These textures are fabricated directly on the substrates using reactive-ion/inductively-coupled plasma etching (RIE/ICP) techniques, and often result in transmitted spectra with no measurable interference effects (fringes) for a wide range of wavelengths. The RIE/ICP processes used in the fabrication process to etch the rARSS is anisotropic and thus well suited for planar components. The improvement in spectral transmission has been found to be independent of optical incidence angles for values from 0° to ±30°. Qualifying and quantifying the rARSS performance on curved substrates, such as convex lenses, is required to optimize the fabrication of the desired AR effect on optical-power elements. In this work, rARSS was fabricated on fused silica plano-convex (PCX) and plano-concave (PCV) lenses using a planar-substrate optimized RIE process to maximize optical transmission in the range from 500 to 1100 nm. An additional set of lenses were etched in a non-optimized ICP process to provide additional comparisons. Results are presented from optical transmission and beam propagation tests (optimized lenses only) of rARSS lenses for both TE and TM incident polarizations at a wavelength of 633 nm and over a 70° full field of view in both singlet and doublet configurations. These results suggest optimization of the fabrication process is not required, mainly due to the wide angle-of-incidence AR tolerance performance of the rARSS lenses. Non-optimized recipe lenses showed low transmission enhancement, and confirmed the need to optimized etch recipes prior to process transfer of PCX/PCV lenses. Beam propagation tests indicated no major beam degradation through the optimized lens elements. Scanning electron microscopy (SEM) images confirmed different structure between optimized and non-optimized samples. SEM images also indicated isotropically-oriented surface structures on both types of lenses.

Details
Author

Taylor, Courtney

Title

Optical performance of random anti-reflection structured surfaces (rARSS) on spherical lenses

Physical Description

1 online resource (155 pages) : PDF

Date

2016

Degree Granting Institution

University of North Carolina at Charlotte

Abstract

Random anti-reflection structured surfaces (rARSS) have been reported to improve transmittance of optical-grade fused silica planar substrates to values greater than 99%. These textures are fabricated directly on the substrates using reactive-ion/inductively-coupled plasma etching (RIE/ICP) techniques, and often result in transmitted spectra with no measurable interference effects (fringes) for a wide range of wavelengths. The RIE/ICP processes used in the fabrication process to etch the rARSS is anisotropic and thus well suited for planar components. The improvement in spectral transmission has been found to be independent of optical incidence angles for values from 0° to ±30°. Qualifying and quantifying the rARSS performance on curved substrates, such as convex lenses, is required to optimize the fabrication of the desired AR effect on optical-power elements. In this work, rARSS was fabricated on fused silica plano-convex (PCX) and plano-concave (PCV) lenses using a planar-substrate optimized RIE process to maximize optical transmission in the range from 500 to 1100 nm. An additional set of lenses were etched in a non-optimized ICP process to provide additional comparisons. Results are presented from optical transmission and beam propagation tests (optimized lenses only) of rARSS lenses for both TE and TM incident polarizations at a wavelength of 633 nm and over a 70° full field of view in both singlet and doublet configurations. These results suggest optimization of the fabrication process is not required, mainly due to the wide angle-of-incidence AR tolerance performance of the rARSS lenses. Non-optimized recipe lenses showed low transmission enhancement, and confirmed the need to optimized etch recipes prior to process transfer of PCX/PCV lenses. Beam propagation tests indicated no major beam degradation through the optimized lens elements. Scanning electron microscopy (SEM) images confirmed different structure between optimized and non-optimized samples. SEM images also indicated isotropically-oriented surface structures on both types of lenses.

Genre

doctoral dissertations

Subjects--Topics

Optics

Degree

Ph.D.

Keywords

Antireflection Coatings
Optical Materials
Optical Properties
Polarization
Subwavelength Structures
Thin Films

Subject Area

Optical Science & Engineering

Advisor(s)

Poutous, Menelaos

Committee Members

Aggarwal, Ishwar
Boreman, Glenn
Evans, Chris
Weldon, Tom

Degree Note

Thesis (Ph.D.)--University of North Carolina at Charlotte, 2016.

Rights Statement

This Item is protected by copyright and/or related rights. You are free to use this Item in any way that is permitted by the copyright and related rights legislation that applies to your use. For other uses you need to obtain permission from the rights-holder(s). For additional information, see http://rightsstatements.org/page/InC/1.0/.

Rights Holder Information

Copyright is held by the author unless otherwise indicated.

Identifier

Taylor_uncc_0694D_11267

Permalink

http://hdl.handle.net/20.500.13093/etd:770